| 牌号Grade | 粒度分布PSD/μm | 化学成分Chemical/% | 检测 频率 Test Frequency |
制成106环 106 Ring 26.9*14.5*11.0mm |
备注Remark | |
| D50 | C | O | 导磁率Permeability （μi） | |||
| T8L | 4.0-6.0 | ≤0.20 | ≤0.50 | 10kHz | ≥55 | |
| T8L-I | 6.0-10.0 | ≤0.20 | ≤0.50 | 10kHz | ≥75 | |
| T8S | 4.0-6.0 | ≤0.20 | ≤0.50 | 10kHz | 25-28 | |
| T2A | 3.0-6.0 | ≤1.50 | ≤1.50 | 200KHz | 9.0-13.0 | |
| T8A3(201) | 3.0-6.0 | ≤0.30 | ≤0.80 | 200kHz | ≥19 | 1g磁环 10.8*6.0*3.0mm |
| T8A5(201) | 5.0-10.0 | ≤0.30 | ≤0.80 | 200kHz | ≥22 | 1g磁环 10.8*6.0*3.0mm |
| T8SK | 4.0-7.0 | ≤0.30 | ≤0.70 | 100kHz | 21.5-25.5 | 绝缘insulation |
| T8SK-B | 5.0-8.0 | ≤0.30 | ≤0.80 | 100kHz | 23.0-27.0 | 绝缘insulation |
| T8A3 | 3.0-6.0 | ≤0.20 | ≤0.60 | 100kHz | 26.0-29.0 | 绝缘insulation |
| T8A3-6JY | 5.0-8.0 | ≤0.20 | ≤0.70 | 100kHz | 27.0-30.0 | 绝缘insulation |
| T8A5 | 3.0-6.0 | ≤0.20 | ≤0.90 | 200kHz | 24.0-29.0 | 绝缘insulation |
| T6A | 1.0-3.0 | ≤1.30 | ≤1.50 | 200kHz | 9.0-11.0 | |
| FeSiCr(-500) | 9.0-13.0 | ≤0.20 | ≤0.65 | 200kHZ | 29-31 | coating |
| FeSiCr(-500)-A | 9-11 | ≤0.20 | ≤0.65 | 200kHz | 27-30 | coating |
| FeSiCr(-500)-B | 10-14 | ≤0.20 | ≤0.80 | 200kHz | 28-31 | coating |
| FeSiCr(-500)-C | 12-17 | ≤0.20 | ≤0.65 | 200kHz | ≥30.5 | coating |
| FeSiCr(-325) | 16.0-20.0 | ＜0.20 | ＜0.60 | 200kHZ | 31-34 | coating |
金属软磁粉芯是以金属软磁粉末为原料，经绝缘包覆处理后，通过粉末冶金工艺制备而成，具有磁电转换和储...
公司现有有效的授权发明专利7项，实用新型专利9项，国际PCT申请专利1项，申请发明专利5项。
9月17-19日，我司参加了在北京国家会议中心举办的WorldPM2018 congress。在会展中心取得傲人成绩，完成...
2018年12月28日上午，第十二届全国人大常委、中国科学技术协会原副主席、中南大学原校长、中国工程院院...