| 牌号（Grade） | 熔体指数(MFI) g/10min | 烧结密度(Sintered density) g/cm3 | 收缩率(OSF) | 磁导率(Permeability | 硬度 (Hardness) | 抗拉强度 （tensile strength）MPa |
屈服强度（Yield Strength）MPa | 伸长率 (Elongation) % |
应用 特性（Application） |
| YWL-17-4PH | ≥600 | ≥7.6 | 1.165±0.003 | ≥260 HV | ≥900 | ≥650 | ≥3 | 常规料 regular | |
| YWL-17-4PH-Z | ≥800 | ≥7.7 | 1.165±0.003 | ≥260 HV | ≥900 | ≥650 | ≥3 | 高密度 High density |
|
| YWL-17-4PH-Z-2 | ≥1000 | ≥7.8 | 1.165±0.003 | ≤1.05 | ≥200 HV | ≥650 | ≥350 | ≥25 | 无磁高抛光 Non-magnetic high polishing |
| YWL-17-4PH-X | ≥600 | ≥7.7 | 1.165±0.003 | ≤1.05 | ≥200 HV | ≥650 | ≥350 | ≥25 | 全氮气无磁高密度Full nitrogen non-magnetic high density |
| YWL-316L | ≥600 | ≥7.8 | 1.165±0.003 | ≤1.06 | 120 HV | ≥500 | ≥160 | ≥45 | 常规料Regular |
| YWL-316L-Z | ≥1000 | ≥7.90 | 1.165±0.003 | ≤1.06 | 120 HV | ≥500 | ≥160 | ≥45 | 高抛光 High polishing |
| YWL-316L-Z-2 | ≥1000 | ≥7.94 | 1.165±0.003 | ≤1.06 | 120 HV | ≥500 | ≥160 | ≥45 | 镜面抛光 Mirror polishing |
| YWL-F75 | ≥1000 | ≥7.85 | 1.165±0.003 | ≤1.01 | ≥240 HV | ≥600 | ≥400 | ≥5 |
| YWL-F75-X | ≥800 | ≥8.0 | 1.165±0.003 | ≤1.01 | ≥240 HV | ≥600 | ≥400 | ≥5 | 高密度 High density |
| YWL-304 | ≥600 | ≥7.7 | 1.165±0.003 | 110 HV | ≥500 | ≥160 | ≥45 | ||
| YWL-304L | ≥600 | ≥7.7 | 1.165±0.003 | 110 HV | ≥500 | ≥160 | ≥45 | ||
| YWL-2507 | ≥600 | ≥7.6 | 1.165±0.003 | ≥260 HV | ≥650 | ≥500 | ≥15 | ||
| YWL-420 | ≥600 | ≥7.5 | 1.165±0.003 | ≥20 HRC | |||||
| YWL-420A | ≥600 | ≥7.5 | 1.165±0.003 | ≥48 HRC | |||||
| YWL-430 | ≥600 | ≥7.6 | 1.165±0.003 | ≥60 HRB | |||||
| YWL-Cr12MoV | ≥600 | ≥7.5 | 1.165±0.003 | ≥40 HRC | |||||
| YWL-0205 | ≥400 | ≥7.5 | 1.216±0.003 | ≥65 HRB | ≥360 | ≥150 | ≥15 | ||
| YWL-4605 | ≥400 | ≥7.5 | 1.216±0.003 | ≥65 HRB | ≥380 | ≥170 | ≥3 | ||
| YWL-03FeNi8 | ≥600 | ≥7.6 | 1.216±0.003 | ≥80 HRB | ≥450 | ≥250 | ≥5 | ||
| YWL-05FeNi8Mo0.5 | ≥400 | ≥7.6 | 1.216±0.003 | ≥40 HRC | ≥800 | ≥450 | ≥3 | ||
| YWL-4140 | ≥600 | ≥7.5 | 1.216±0.003 | ≥70 HRB | ≥600 | ≥350 | ≥3 | ||
| YWL-4340 | ≥600 | ≥7.5 | 1.216±0.003 | ≥70 HRB | ≥700 | ≥500 | ≥5 | ||
| YWL-8740 | ≥600 | ≥7.45 | 1.216±0.003 | ≥75 HRB | ≥800 | ≥450 | ≥3 | ||
| YWL-8620 | ≥600 | ≥7.45 | 1.216±0.003 | ≥70 HRB | ≥450 | ≥300 | ≥10 | ||
| YWL-8620-L | ≥600 | ≥7.60 | 1.216±0.003 | ≥70 HRB | ≥450 | ≥300 | ≥10 | 高密度 High density |
金属软磁粉芯是以金属软磁粉末为原料，经绝缘包覆处理后，通过粉末冶金工艺制备而成，具有磁电转换和储...
公司现有有效的授权发明专利7项，实用新型专利9项，国际PCT申请专利1项，申请发明专利5项。
9月17-19日，我司参加了在北京国家会议中心举办的WorldPM2018 congress。在会展中心取得傲人成绩，完成...
2018年12月28日上午，第十二届全国人大常委、中国科学技术协会原副主席、中南大学原校长、中国工程院院...